- Description
Product Detail
Typical properties (Note: not for specification purpose)
Gumstock properties
Grade | HF-A361C | HF-F2462P | HF-A401C | HF-F2602AP |
Solubility | soluble in low molecular weight ketones, some ester | |||
Chlorine Content, % | 66 | 69 | 66 | 66 |
Specific Gravity | 1.82 | 1.88 | 1.82 | 1.82 |
Mooney Viscosity ML 1+10 @ 121 OC | 30 | 40 | 42 | 38 |
Recommended Vulcanization Formulation for test | Precompounds 100 phr MT Carbon Black (N 990) 30 phr Ca(OH)2 6 phr MgO 3 phr |
Rheological Properties (moving die rheometer, 177oC, 6 min.)
Grade | HF-A361C | HF-F2462P | HF-A401C | HF-F2602AP |
ML, N.m | 0.22 | 0.28 | 0.30 | 0.31 |
MH, N.m | 1.95 | 1.66 | 2.92 | 2.29 |
T90 | 1'49" | 1'57" | 1'55" | 1'55" |
Ts2 | 0'59" | 0'52" | 0'55" | 0'57" |
Physical properties of vulcanizate
Grade | HF-A361C | HF-F2462P | HF-A401C | HF-F2602AP |
press cure | 6 min. @177oC | |||
post cure | 24hr. @ 230oC | 24hr. @ 230oC / 12hr. @ 200oC | ||
Tensile Strength, MPa | 14.3 | 14.0 | 14.0 | 14.0 / 13.0 |
Elongation at Break, % | 230 | 240 | 190 | 230 / 240 |
Hardness, Shore A | 77 | 79 | 77 | 76 |
Compression Set after 70hr. @ 200oC aging, % | 16 | 14 | 15 | 16 |
Main grades and Applications
HF-A361C:
Excellent mold flow, good metal bonding and scorch safety
Improved mold release, less mold fouling
Recommended for compression or transfer molding of O-rings, gaskets.
HF-A401C:
Excellent mold release, good scorch safety
Recommended for compression or transfer molding of O-rings, gaskets.
HF-F2462P:
Excellent mold release, good scorch safety.
Recommended for sealing applications that require improved solvent resistance and permeation resistance to fuels, also for fuel tube extrusion
HF-F2602AP:
Excellent mold flow, easier mold release, good scorch safety
Recommended for sealing articles with multi-configuration
Shanghai Fluorochem Industry Co.,Ltd supply high quality Precompound FKM, we can also customize Precompound FKM as per customer's different requirements.
Processing
•Our precompounds could be mixed with conventional fillers and other aids by rubber processing equipment.
•Fillers and other additives should be mixed uniformly, then added in precompounds
Processing methods: compression molding, transfer molding. Additionally, F2462P and F2602AP could be used in extrusion, A361C could be used in injection molding
Package:
Net 25kgs in cardboard cartons.
- FKM Powder 15 Pieces / (Min. Order)
- FKM Compound 15 Pieces / (Min. Order)
- FKM Copolymer Gum 15 Pieces / (Min. Order)
- Polymer Processing Aid PPA9028 15 Pieces / (Min. Order)
- Polymer Processing Aid PPA9024 15 Pieces / (Min. Order)
- Polymer Processing Aid PPA9023 15 Pieces / (Min. Order)
- Polymer Processing Aid PPA9022 15 Pieces / (Min. Order)
- Fluorocarbon Solvent 15 Pieces / (Min. Order)
- Tetrafluoroethane B-Sultone 15 Pieces / (Min. Order)
- Perfluoro-3,6-Dioxa-4-Methyl-7-Octyl Sulfonyl Fluoride 15 Pieces / (Min. Order)
- Difluoroethylene 15 Pieces / (Min. Order)
- Hexafluoropropane Qxide 15 Pieces / (Min. Order)
- PTFE Wax For Water-Based Coating & Ink 15 Pieces / (Min. Order)
- PTFE Wax For Coating 15 Pieces / (Min. Order)
- PTFE Micropowder For Engineering Plastics & Rubber 15 Pieces / (Min. Order)
- FKM Powder 15 Pieces / (Min. Order)
- FKM Compound 15 Pieces / (Min. Order)
- FKM Copolymer Gum 15 Pieces / (Min. Order)
- PVDFMembrane Grade-Powder 15 Pieces / (Min. Order)
- FEP Powder 15 Pieces / (Min. Order)
- FEP Resin 15 Pieces / (Min. Order)
- PTFE Aqueous Dispersion 15 Pieces / (Min. Order)